Dental Materials
Volume 22, Issue 8 , Pages 785-791 , August 2006

A new kinetic model for the photopolymerization shrinkage-strain of dental composites and resin-monomers

  • Mohammad Atai

      Affiliations

    • Iran Polymer and Petrochemical Institute (IPPI), P.O. Box 14965/115, Tehran, Iran
    • Corresponding Author InformationCorresponding author. Tel.: +9821 44580085; fax: +9821 44580023.
    • ,
  • David C. Watts

      Affiliations

    • Biomaterials Science Research Group, School of Dentistry and Photon Science Institute, The University of Manchester, Manchester M15 6FH, UK

Received 17 January 2006 ,Revised 25 January 2006 ,Accepted 1 February 2006.

References 

  1. Ahn K-D, Chung C-M, Kim Y-H. Synthesis and photopolymerization of multifunctional methacrylates derived from Bis-GMA for dental applications. J Appl Polym Sci. 1999;71:2033–2037
  2. Klee JE, Neidhart F, Flammersheim H-J, Mulhaupt R. Monomers for low shrinking composites, 2a: synthesis of branched methacrylates and their application in dental composites. Macromol Chem Phys. 1999;200:517–523
  3. Chung C-M, Kim J-G, Kim M-S, Kim K-M, Kim K-N. Development of a new photocurable composite resin with reduced curing shrinkage. Dent Mater. 2002;18:174–178
  4. Chung C-M, Kim M-S, Kim J-G, Jang D-O. Synthesis and photopolymerization of trifunctional methacrylates and their application as dental monomers. J Biomed Mater Res. 2002;62:622–627
  5. Khatri CA, Stansbury JW, Schultheisz CR, Antonucci JM. Synthesis, characterization and evaluation of urethane derivatives of Bis-GMA. Dent Mater. 2003;19:584–588
  6. Kim Y, Kim CK, Cho BH, Son HH, Um CM, Kim OY. A new resin matrix for dental composite having low volumetric shrinkage. J Biomed Mater Res Part B: Appl Biomater. 2004;70B:82–90
  7. Chen M-H, Chen C-R, Hsu S-H, Sun S-P, Su W-F. Low shrinkage light curable nanocomposite for dental restorative material. Dent Mater. 2006;22(2):138–145
  8. Satsangi N, Rawls HR, Norling BK. Synthesis of low-shrinkage polymerizable liquid-crystal monomers. J Biomed Mater Res Part B: Appl Biomater. 2004;71B:153–158
  9. Watts DC, Al Hindi A. Intrinsic ‘soft-start’ polymerization shrinkage-kinetics in an acrylate-based resin-composite. Dent Mater. 1999;15:39–45
  10. Lim B-S, Ferracane JL, Sakaguchi RL, Condon JR. Reduction of polymerization contraction stress for dental composites by two-step light-activation. Dent Mater. 2002;18:436–444
  11. Condon JR, Ferracane JL. Reduction of composite contraction stress through non-bonded microfiller particles. Dent Mater. 1998;14:256–260
  12. Condon JR, Ferracane JL. Reduced polymerization stress through non-bonded nanofiller particles. Biomaterials. 2002;23:3807–3815
  13. Torstenson B, Oden A. Effects of bonding agent types and incremental techniques on minimizing contraction gaps around resin composites. Dent Mater. 1989;5(4):218–223
  14. Prati C, Montanari G. Comparative microleakage study between the sandwich and conventional three-increment techniques. Quintessence Int. 1989;20(8):587–594
  15. Saunders WP, Strang R, Ahmad I. Effect of composite resin placement and use of an unfilled resin on the microleakage of two dentin bonding agents. Am J Dent. 1990;3(4):153–156
  16. Krejci I, Lutz F. Marginal adaptation of Class V restorations using different restorative techniques. J Dent. 1991;19(1):24–32
  17. Crim GA. Microleakage of three resin placement techniques. Am J Dent. 1991;4(2):69–72
  18. Santini A, Plasschaert AJ, Mitchell S. Effect of composite resin placement techniques on the microleakage of two self-etching dentin-bonding agents. Am J Dent. 2001;14(3):132–136
  19. St Georges AJ, Wilder AD, Perdigao J, Swift EJ. Microleakage of Class V composites using different placement and curing techniques: an in vitro study. Am J Dent. 2002;15(4):244–247
  20. Mullejans R, Lang H, Schuler N, Baldawi MO, Raab WH. Increment technique for extended Class V restorations: an experimental study. Oper Dent. 2003;28(4):352–356
  21. Loguercio AD, Reis A, Ballester RY. Polymerization shrinkage: effect of constraint and filling technique in composite restorations. Dent Mater. 2004;20(3):236–243
  22. Cook WD. Photopolymerization kinetics of dimethacrylates using the camphorquinone/amine initiator system. Polymer. 1992;33(3):600–609
  23. Maffezzoli A, Della Pietra A, Rengo S, Nicolais L, Valletta G. Photopolymerization of dental composite matrices. Biomaterials. 1994;15(15):1221–1228
  24. Nie J, Rabek JF, Linden L-A. Photopolymerization of poly (melamine-co-formaldehyde) acrylate for dental restorative resins. Polym Int. 1999;48:129–136
  25. Khudyakov IV, Legg JC, Purvis MB, Overton BJ. Kinetics of photopolymerization of acrylates with functionality of 1-6. Ind Eng Chem Res. 1999;38:3354–3359
  26. Lee IB, Um CM. Thermal analysis on the cure speed of dual cured resin cements under porcelain inlays. J Oral Rehab. 2001;28:186–197
  27. Stansbury JW, Dickens SH. Network formation and compositional drift during photo-initiated copolymerization of dimethacrylate monomers. Polymer. 2001;42:6363–6369
  28. Atai M, Watts DC, Atai Z. Shrinkage strain-rates of dental resin-monomer and composite systems. Biomaterials. 2005;26:5015–5020
  29. Kamal MR, Sourour S. Kinetic and thermal characterization of thermoset cure. Polym Eng Sci. 1973;13(1):59–64
  30. Kamal MR. Thermoset characterization for moldability analysis. Polym Eng Sci. 1974;14(3):231–239
  31. Söderholm KJM. Influence of silane treatment and filler fraction on thermal expansion of composite resins. J Dent Res. 1984;63(11):1321–1326
  32. Li Y, Swartz ML, Philips RW, Moore BK, Roberts TA. Effect of filler content and size on the properties of composites. J Dent Res. 1985;64(12):1396–1401
  33. Germain SST, Swartz ML, Philips RW, Moore BK, Roberts TA. Properties of microfilled composite resins as influenced by filler content. J Dent Res. 1985;64(2):155–160
  34. Chung K-H, Greener EH. Correlation between degree of conversion, filler concentration and mechanical properties of posterior composite resins. J Oral Rehab. 1990;17:487–494
  35. Taylor DF, Kalachandra S, Sankarapandian M, McGrath JE. Relationship between filler and matrix resin characteristics and the properties of uncured composite pastes. Biomaterials. 1998;19:197–204
  36. Kobayashi M, Shinzato S, Kawanabe K, Neo M, Matsushita M, Kokubo T, et al. Alumina powder/Bis-GMA composite: effect of filler content on mechanical properties and osteoconductivity. J Biomed Mater Res. 2000;49:319–327
  37. Lim B-S, Ferracane JL, Condon JR, Adey JD. Effect of filler fraction and filler surface treatments on wear of micro filled composites. Dent Mater. 2002;18:1–11
  38. Atai M, Nekoomanesh M, Hashemi SA, Amani S. Physical and mechanical properties of an experimental dental composite based on a new monomer. Dent Mater. 2004;20:663–668
  39. Watts DC, Cash AJ. Kinetic measurements of photo-polymerization contraction in resins and composites. Meas Sci Technol. 1991;2:788–794
  40. Lovell LG, Stansbury JW, Syrpes DC, Bowman CN. Effects of composition and reactivity on the reaction kinetics of dimethacrylate/dimethacrylate copolymerizations. Macromolecules. 1999;32:3913–3921
  41. Andrzejewska E. Photopolymerization kinetics of multifunctional monomers. Prog Polym Sci. 2001;26:605–665
  42. Watts DC. Reaction kinetics and mechanics in photo-polymerised networks. Dent Mater. 2005;21:27–35
  43. Odian G. Principle of polymerization. 2nd ed.. John Wiley & Sons, Inc.; 1981;
  44. Anseth KS, Wang CM, Bowman CN. Kinetic evidence of reaction diffusion during the polymerization of multi (meth) acrylate monomers. Macromolecules. 1994;27:650–655
  45. Andrzejewska E, Linden L-A, Rabek JF. Modelling the kinetics of photoinitiated polymerization of di(meth)acrylates. Polymer Int. 1997;42:179–187
  46. Maffezzoli A, Terzi R. Effect of irradiation intensity on the isothermal photopolymerization kinetics of acrylic resins for stereolithography. Thermochim Acta. 1998;321:111–121
  47. Lecamp L, Youssef B, Bunel C, Lebaudy P. Photoinitiated polymerization of dimethacrylate oligomers: 2. Kinetic studies. Polymer. 1999;40:1403–1409
  48. Waters DN, Paddy JL. Equations for isothermal differential scanning calorimetric curves. Anal Chem. 1988;60:53–57
  49. Weinmann W, Thalacker C, Guggenberger R. Siloranes in dental composites. Dent Mater. 2005;21:68–74
  50. Halvorson RH, Erickson RL, Davidson CL. The effect of filler and silane content on conversion of resin-based composite. Dent Mater. 2003;19:327–333
  51. Technical bulletin pigments, no. 11. Basic characteristic of AEROSIL®. 5th ed. Germany: Degussa; 1997.

PII: S0109-5641(06)00048-0

doi: 10.1016/j.dental.2006.02.009

Dental Materials
Volume 22, Issue 8 , Pages 785-791 , August 2006

Article Tools

* Image Usage & Resolution